EPO W TRASPARENTE
Epoxy filler based on water
Good mechanical and chemical resistance
Solvent - free, odourless
Code
1217
Description
Amine - epoxy paint based on water with high permeability to water vapour
Use
This product is suitable for the anti - dust treatment of concrete floors or as a primer in solvent - less or water - based epoxy cycles, as a binder for inert quartz aggregates to perform multilayer cycles.
It can be applied on concrete that is not perfectly dry or on substrates with problems of the damp rising.
It can be applied on concrete that is not perfectly dry or on substrates with problems of the damp rising.
Appearance of the film
Matt - semi - glossy (it depends on the thickness)
Color
Transparent
Components
2
Hardening
Chemical reaction between two components
Specific weight
1,050 gr/ml (A + B)
Volume of solids
50%
VOC
0 gr/ liter
Minimum thickness
40 micron
Estimated yield
12,5 m² / litre for a thickness of 40 micronsi
Flash point
Component A > 113°C
Component B > 115°C
Component B > 115°C
Adhesion
On concrete 2,5MPa On stoneware 12MPa ASTM D 4541
Abrasion resistance
70 mg ASTM D 4060 wheel CS 17 1 Kg 1000 cycles
Temperature resistance
Da -20 a + 100°C
Chemical resistance
Water, cleansing products, oils, fuels. It is not suitable for acid solutions and solvents.
Preparation of surfaces
Concrete:
Chemical washing in order to remove laitance layers, efflorescence and other types of pollutants which may affect the adhesion
Chemical washing in order to remove laitance layers, efflorescence and other types of pollutants which may affect the adhesion
Preparation of the product
Mix the product according to the following ratio by weight:
Component A : 100
Component B: 40
Mix Component A separately and then add Component B
For applications in multilayered cycles, add 60 - 70 % of quartz 0,1 - 0,5 while stirring continuously.
Component A : 100
Component B: 40
Mix Component A separately and then add Component B
For applications in multilayered cycles, add 60 - 70 % of quartz 0,1 - 0,5 while stirring continuously.
Induction time
Not expected
Pot life
2 hours at 20° C
Thinning
As first coat, dilute with 80 % of water; as second coat, dilute with 50 % of water
Environmental conditions
Ambient temperature: from + 5 to 35° C
Temperature of the support: > 10° C
Humidity: 0 - 70 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point
Temperature of the support: > 10° C
Humidity: 0 - 70 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point
Drying and hardening time
For the thickness of 40 microns (wet) 10° C 20° C 30° C
Dry to touch 6 3 2 hours
Dry in depth 10 6 4 hours
Dry to touch 6 3 2 hours
Dry in depth 10 6 4 hours
Time of overpainting
Minimum (hours) 10° C 20° C 30° C
10 8 5 hours
Maximum (days) 7
10 8 5 hours
Maximum (days) 7
Application
Brush, roller, airless, spray
If you use the brush, you have to use nylon or pure bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, use the method of crossing coats.
Airless:
Nozzle size: 0,46 mm (0,018 inch)
Air pressure: 150 bar
If you use the brush, you have to use nylon or pure bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, use the method of crossing coats.
Airless:
Nozzle size: 0,46 mm (0,018 inch)
Air pressure: 150 bar
Shelf life
2 years in a cool and dry place (max 40° C)
Packs
Comp A 10 kg Comp B 4 Kg