Code
0213
Description
It is an epoxy - polyamide primer: it has an effective anti - corrosive action with barrier effect and it adheres on many substrates such as aluminum, fiberglass, galvanized sheet metal, and so on
Use
This product is used as a primer for epoxy and polyurethane cycles in environments with medium and high aggressiveness.
Appearance of the film
Matt
Color
Grey
Components
2
Hardening
Chemical reaction between two components
Specific weight
1,410 gr/ml (A + B)
Volume of solids
56%
Voc
540 gr/ liter
Minimum thickness
75 micron
Resa teorica
Estimated yield
Flash point
Component A 27°C
Component B 34°C
Thinner 27°C
Component B 34°C
Thinner 27°C
Adhesion
On sandblasted steel: 8MPa, on brushed metal 4MPa
Abrasion resistance
65 mg CS 17 1 Kg 1000 cycles
Salt spray resistance
> 1500 ore
Temperature resistance
Max 120° C continuously, 200° C discontinuously
Preparation of surfaces
Oxidised steel without calamine:
Mechanical cleaning at the grade St3, of Svensk Standard SIS 1967 for cycles that are not subject to immersion.
SA 2 ½ sandblasting for cycles that are subject to immersion
Mechanical cleaning at the grade St3, of Svensk Standard SIS 1967 for cycles that are not subject to immersion.
SA 2 ½ sandblasting for cycles that are subject to immersion
Preparation of the product
Mix the product according to the following ratio by weight:
Component A : 100
Component B: 15
Mix Component A separately and then add Component B and mix together
Component A : 100
Component B: 15
Mix Component A separately and then add Component B and mix together
Thinning
5 - 10 % with an epoxy thinner depending on the applications
Induction time
Not expected
Pot life
> 8 hours a 20°C
Environmental conditions
Ambient temperature: from + 10 to 35° C
Temperature of the support: > 10° C
Humidity: 0 - 70 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Temperature of the support: > 10° C
Humidity: 0 - 70 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Drying and hardening time
For the thickness of 100 microns (wet) 10° C 20° C 30° C
Dry to touch 6 3 2 hours
Dry in depth 10 6 4 hours
Dry to touch 6 3 2 hours
Dry in depth 10 6 4 hours
Time of overpainting
Minimum (hours) 10° C 20° C 30° C
10 8 5 hours
Maximum (months) 1
10 8 5 hours
Maximum (months) 1
Application
Brush, roller, airless, spray
If you use the brush, you have to use nylon or pure bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, use the method of crossing coats.
Airless:
Nozzle size: 0,46 mm (0,018 inch)
Air pressure: 150 bar
If you use the brush, you have to use nylon or pure bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, use the method of crossing coats.
Airless:
Nozzle size: 0,46 mm (0,018 inch)
Air pressure: 150 bar
Shelf life
2 years in a cool and dry place (max 40° C)
Packs
Kg. 11,500 (10+1,500)
Kg. 4,600 (4 + 0,600)
Kg. 1,150 (1 + 0,150)
Kg. 4,600 (4 + 0,600)
Kg. 1,150 (1 + 0,150)