Solvent - based paint made of modified vinyl acrylic resins, with high resistance to the atmospheric agents, alkali and with a good permeability to water vapour.
Use
This product is applied on different substrates such as: plaster, lime plaster, bituminous surfaces, fibre cement.
Appearance of the film
Semi - glossy
Color
White, red and color chart
Component
1
Hardening
Physical hardening through evaporation of solvents
Specific weight
1,3 – 1,4 gr/ml
Volume of solids
45 %
VOC
480 gr/ liter
Minimum thickness
60 -80 micron
Estimated yield
7,5 m² / litre for a thickness of 60 microns
Flash point
Component A 34°C Thinner 34°C
Temperature resistance
Max 110° C continually 200° C discontinuously
Preparation of surfaces
New metal supports: Remove dust and contaminants, such as greases and oils, from the surfaces. For new concrete Adequate dust removal: application of a diluted coat, followed after 24 hours by an other coat as it is
Preparation of the product
Mix the product before the use and add the thinner Component A 100 Thinner max 20 % - 30 % (First coat)
Environmental conditions
Ambient temperature: from + 5 to 40° C Temperature of the support: > 10° C Humidity: 0 - 85 % In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point
Drying and hardening time
For the thickness of 60 microns 10° C 20° C 30° C Dry to touch 6 3 2 hours Dry in depth 48 24 10 hours
Time of overpainting
Minimum (hours) 10° C 20° C 30° C 24 12 6 hours Maximum unlimited in the absence of contaminants
Application
Brush, roller, spray If you use the brush, you have to use nylon or natural bristle brushes. If you use the roller, you have to use medium - haired rollers. For the application, it is necessary to use the method of crossing coats