Oleophenolic primer which has a dual anti - corrosive action, chemical and with barrier effect.
Use
Primer for sandblasted steel at the grade SA 2 or brushed steel according to the grade CST3 of Sensk Standard SIS 1967. It is covered with synthetic finishes such as “Resing”, “Toplac”, “Novolux”, “Resilux”.
Appearance of the film
Matt
Color
Red, grey
Component
1
Hardening
Physical hardening through evaporation of solvents and oxidative polymerization
Specific weight
1,520 gr/ml
Volume of solids
61 %
VOC
306 gr/ liter
Minimum thickness
40 – 50 micron
Estimated yield
15 m² / liter for a thickness of 40 microns
Flash point
Component A 34°C Thinner 34°C
Temperature resistance
100° C continuously, 140 ° C discontinuously.
Salt spray resistance
Thickness 80 microns 1000 hours, neither blistering, nor propagation of rust.
Preparation of surfaces
New steel: SA 2 sandblasting or brushing, in any case clean surfaces. Old paints: Brushing, dust removal
Preparation of the product
Mix the product before the use and add the thinner Component A 100 Thinner 5 - 10 % depending on the thickness of the dry film to be applied
Environmental conditions
Ambient temperature: from + 5 to 40° C Temperature of the support: > 10° C Humidity: 0 - 85 % In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Drying and hardening time
For the thickness of 45 microns 10° C 20° C 30° C Dry to touch 6 3 2 hours Dry in depth 48 24 10 hours
Time of overpainting
Minimum (hours) 10° C 20° C 30° C 24 12 6 hours Maximum unlimited in the absence of contaminants
Application
Brush, roller, spray If you use the brush, you have to use nylon or natural bristle brushes. If you use the roller, you have to use medium - haired rollers. For the application, it is necessary to use the method of crossing coats.