SILOX INTONACHINO
BRANDED PRODUCT CE EN 15824
Permeable to water vapour
Water - repellent, anti - mold and anti - algae
Code
0855
Description
Wall coating based on modified acrylic resins with silicone resins, natural fibers, granular marble that give the product, after complete drying, impermeability to the weather and to the atmospheric agents, and resistance to molds and lichens. Even if the wall is breathable, it is a water - repellent and waterproof material.
Use
This product is applied on old and new plasters based on hydraulic binders as a filler and as a smoothing agent of the substrate. It can be used on old organic and mineral paints, as long as they are absorbent and united
Appearance of the film
Matt
Color
White
Vapour permeability coefficient
V2
Absorption of water
W2
Vapour permeability and water repellency according to the regulation DIN 18550
Sd x w24 = 0,066 Kg/m/h 0,5 < 0,2 Kg/m/ h 0,5. It presents high ageing stability, high resistance to chemical aggressive elements and performance characteristics of vapour permeability and water repellency that meet the rule DIN 18550 and the rule NFT 30 - 808 3.2.1.
Adhesion
1.1 MPa
Durability
1.3 MPa
Thermal conductivity
(10, dry) 1.17 W/m k (value table; P=50%)
Fire reaction
Euroclass F
Hardening
Physical hardening through evaporation of water and union of the polymer
specific weight
From 1,620 gr/ml
VOC
25 gr/ liter
Thickness of the film
1,2 mm= 1200 micorn
1,5 mm= 1500 micron
1,5 mm= 1500 micron
Estimated yield
0,7-1,2= Kg. 1,800 kg/mq. (270)
1,2 mm= Kg. 2,500 kg/mq. (300)
1,2 mm= Kg. 2,500 kg/mq. (300)
Preparation of the product
Mix the product before the use
Component A 100
Component A 100
Preparation of surfaces
New surfaces:
Dry and mature. Remove any efflorescence by brushing or washing.
Old surfaces:
Remove dust and all old paints that are peeling off, widen any cracks and fill them with a filler. Eliminate completely old lime or tempera paints.
In the presence of molds, provide an appropriate anti - mold treatment.
Prime the surfaces with an acrylic fixative.
Dry and mature. Remove any efflorescence by brushing or washing.
Old surfaces:
Remove dust and all old paints that are peeling off, widen any cracks and fill them with a filler. Eliminate completely old lime or tempera paints.
In the presence of molds, provide an appropriate anti - mold treatment.
Prime the surfaces with an acrylic fixative.
Environmental conditions
Ambient temperature: from + 8 to 40° C
Temperature of the support: > 5° C
Humidity: 0 - 75 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Temperature of the support: > 5° C
Humidity: 0 - 75 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Precautions:
Do not apply in the presence of surface condensation or under direct sunlight.
The humidity of the substrate must be less than 10 %.
Protect from the rain for at least 48 hours.
The complete drying of the product and the polymerization process takes place in 10 - 15 days under optimal environmental conditions. If, in the meantime, there were rains that would somehow wet the product, unsightly dregs with a glossy and sticky appearance could appear. They could be eliminated by power wash or waiting for the next rains. This phenomenon does not affect the characteristics of the product.
The humidity of the substrate must be less than 10 %.
Protect from the rain for at least 48 hours.
The complete drying of the product and the polymerization process takes place in 10 - 15 days under optimal environmental conditions. If, in the meantime, there were rains that would somehow wet the product, unsightly dregs with a glossy and sticky appearance could appear. They could be eliminated by power wash or waiting for the next rains. This phenomenon does not affect the characteristics of the product.
Drying and hardening time
At 25° C from 1 to 3 hours depending on the thickness applied
Application
Plastic trowel
Spread the product on the substrate in an homogeneous way and make it uniform before filiation begins.
Spread the product on the substrate in an homogeneous way and make it uniform before filiation begins.
Shelf life
1 year in a cool and dry place (max 40° C)
Packs
Comp A Kg. 25