SILOX PRIMER
Fixative based on polysiloxanes
Water - repellent consolidating product
Code
0601
Description
Fixative based on polysiloxanes and acrylic resins
Use
This product is used for the consolidation and impregnation of mineral substrates, that are poorly absorbent.
It does not change the breathability of the substrate and it has a good consolidating power.
It can be applied on new and old plasters, old organic or mineral paints, as long as they are well adherent
It does not change the breathability of the substrate and it has a good consolidating power.
It can be applied on new and old plasters, old organic or mineral paints, as long as they are well adherent
Appearance of the film
Matt
Component
1
Hardening
Physical hardening through evaporation of water and union of the polymer
Specific weight
From 1,130 gr/ml
VOC
10 gr/ liter
Estimated yield
18 - 20 m² / litre for thicknesses with medium porosity
Flash point
Component A > 114°C
Preparation of surfaces
Plasters:
Make sure that the substrate has passed a maturation time of 28 days and that its humidity is less than 10 %.
Remove any efflorescence by washing and brushing.
Old paints based on tempera or lime should be removed.
Make sure that the substrate has passed a maturation time of 28 days and that its humidity is less than 10 %.
Remove any efflorescence by washing and brushing.
Old paints based on tempera or lime should be removed.
Preparation of the product
Product ready to use. Mix the product before the use.
Component A 100
Water 25 - 30 %
Component A 100
Water 25 - 30 %
Environmental conditions
Ambient temperature: from + 5 to 40° C
Temperature of the support: > 10° C
Humidity: 0 - 75 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Avoid the application in the presence of excessive condensation or under direct sunlight
Temperature of the support: > 10° C
Humidity: 0 - 75 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Avoid the application in the presence of excessive condensation or under direct sunlight
Drying and hardening time
10° C 20° C 30° C
Dry to touch 6 2 1 hours
Dry in depth 18 12 6 hours
Dry to touch 6 2 1 hours
Dry in depth 18 12 6 hours
Time of overpainting
Minimum (hours) 10° C 20° C 30° C
18 12 6 hours
Maximum unlimited in the absence of contaminants
18 12 6 hours
Maximum unlimited in the absence of contaminants
Application
Brush, roller
If you use the brush, you have to use nylon or natural bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, it is necessary to use the method of crossing coats.
If you use the brush, you have to use nylon or natural bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, it is necessary to use the method of crossing coats.
Shelf life
1 year in a cool and dry place (min 5° C - max 35° C)
Packs
Lt. 20, Lt. 5 , Lt. 1