SPATOLATO EXTRA

Code

902

Description

Plastic quartz coating for internal and external places made of siliceous aggregates, granular marble, water emulsion of a 100 % acrylic copolymer and various pigments. The pigments chosen, that are among the best on the market, guarantee the color tightness over time. Even if the product is breathable, the wall surface is water - repellent and waterproof.

Use

This product is used when you want a high resistance coating with a good appearance. Its characteristics have a particular resistance to the impacts, to the abrasions, a high degree of resistance to the climatic and atmospheric agents.

Appearance of the film

Matt

Color

White - color chart

Component

1

Hardening

Physical hardening through evaporation of water and union of the polymer

Vapour permeability coefficient

V2

Specific weight

From 1,380 gr/ml

Absorption of water

W2

volume of solids

51 %

Adhesion

1.1 MPa

VOC

120 gr/ liter

Durability

1.3 MpA

Thickness of the film

1 mm= 1000 micron
1,2 mm= 1200 micorn
1,5 mm= 1500 micron

Thermal conductivity

(10,dry) 1.17 W/m*k (tab.valore; P=50%)

Estimated yield

1 mm= Kg. 1,500 kg/mq (200).
0,7-1,2= Kg. 1,800 kg/mq. (270)
1,2 mm= Kg. 2,500 kg/mq. (300)
1,5 mm= Kg. 2,800 kg/mq. (400)

Fire reaction

Euroclass F

flash point

Component A > 114°C

Elongation %

200 for a dry thickness of 500 microns

Washability

> 10000 washes

Preparation of surfaces

New surfaces: remove any traces of dirt and of efflorescence and prime with our product « PRIMER P/PIGMENTATO »
Old surfaces: make sure that the old plaster is well adherent and, in the case of cracks, treat the substrate with our « FONDO ELASTICO FIBRATO ».

Preparation of the product

Mix the product before the use.
For applications with a spatula, the product should not be diluted or with maximum 2 % of water.

Environmental conditions

Ambient temperature:                from + 5  to  40° C
Temperature of the support:       > 10° C
Humidity:                                    0 - 85 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.

Drying and hardening time

For the thickness of 200 microns           10° C           20° C           30° C
Dry to touch                                            24                6                   1    hours
Dry in depth                                            24                8                   2    hours

Time of overpainting

Minimum  (hours)                                    10° C          20° C            30° C
                                                                 24              8                   3 hours
Maximum    unlimited in the absence of contaminants

application

Spread the product with a steel spatula and smooth with a plastic trowel

Shelf life

1 year in a cool and dry place (max 40° C)

Packs

Comp A Kg. 24,000